Related Metals: Nickelvac 201(tm), VDM LC Nickel 99.2(tm), Ametek 899E(tm), AL 201(tm), LC Nickel(tm), CM 201(tm), VDM LC 99.2(tm).
Specifications: AMS 5553, ASTM B160, ASTM B161, ASTM B162, ASTM B163, ASTM B366, ASTM B725, ASTM B730, DIN 2.4061, DIN 2.4068, UNS N02201.
Principal Design Features This is a lower carbon version of commercially pure (99%) nickel. The material does contain minor amounts of other elements, totaling less than 1%.
Applications Electronic components, applications where spinning to form the product is especially desired. Chemical corrosion resistance in caustic solutions.
Machinability is basically the same as for Nickel 200. The 201 variety is softer and "gummy" but can be readily machined by conventional mean. High-speed-steel tools are recommended.
Easily formed by conventional methods. Nickel 201 is especially well suited to forming parts by spinning.
Corrosion ResistanceThe low carbon content of Nickel 201 enhances its corrosion resistance in comparison to Nickel 200. It is very good for use with caustic soda, dry fluorine, and chlorine or hydrogen chloride, even at elevated temperatures.
WeldingWeldable by standard means as was also the case with Nickel 200. However oxyacetylene welding should NOT be used with Nickel 201.
Heat Treatment Anneal at 1650 F to 1300 F depending upon the degree of cold working and time at temperature.
Forging Forging should be done in the range of 2100 F to 1200 F.
Hot working may be done in the range of 2100 F to 1200 F.
Cold working is readily accomplished with standard tooling.
Anneal at 1650 F to 1300 F depending upon time at temperature and amount of cold working that has been done.
Hardens only by cold working.